couple of hours back at tig after 14 years
Posted: Tue May 06, 2014 10:54 pm
- tig may 4.jpg (23.75 KiB) Viewed 556 times
Welding Tips and Tricks
The Forum
https://forum.weldingtipsandtricks.com/
couple of hours back at tig after 14 years
https://forum.weldingtipsandtricks.com/viewtopic.php?f=5&t=5083
Page 1 of 1
please critique be harsh tell me what I can do to improve
Re: couple of hours back at tig after 14 years
Posted: Tue May 06, 2014 11:07 pm
It's like riding a bike 
Great job there!! Not many can get a good ripple and decent consistency down after that long. I will only offer one critique, and we try out best not to be harsh, add one of two more dips when you get to the end of your weld and back off slowly. This will eliminate the crater at the end of the weld. Other than that, practice, practice, practice.
-Jonathan
Great job there!! Not many can get a good ripple and decent consistency down after that long. I will only offer one critique, and we try out best not to be harsh, add one of two more dips when you get to the end of your weld and back off slowly. This will eliminate the crater at the end of the weld. Other than that, practice, practice, practice.-Jonathan
Re: couple of hours back at tig after 14 years
Posted: Tue May 06, 2014 11:08 pm
thanks ill try that on break tomorrow
Re: couple of hours back at tig after 14 years
Posted: Tue May 06, 2014 11:22 pm
not that I can do any better, but to get real critique you need to slice it down the middle perpendicular to the weld bead direction in order to see the penetration into the root of the joint. THAT is what tells all, pretty beads aside.
Re: couple of hours back at tig after 14 years
Posted: Wed May 07, 2014 5:42 pm
Drop the lid and let it eat. I was away for over 20 years.
Give it 50 hours.
Give it 50 hours.