[smaliden2]

in the first pic I think my welds are starting to look a lilttle better. The second pic is the back side, and I dont know if thats how it is supposed to look or if I just used too much heat. I am finally getting to the point where I can see the etching zone and see when things are starting to go wrong. The welds are on .025 aluminum plate.

CAM00334b.jpg (99.66 KiB) Viewed 799 times

CAM00335b.jpg (76.58 KiB) Viewed 799 times

[Superiorwelding]

I personally think you are doing great. .025 is some very thin material to practice on. Keep up the hood time.

-Jonathan

[nathan]

Yeah, man if you can control it on .025, you're set! when did you start working on TIG aluminum?

[RichardH]

Yeah, man if you can control it on .025, you're set!

No joke. The fact that you're not blowing holes in the sheet is impressive by itself. For running beads, I'd probably use a piece of 1/8" at least, to avoid too many "learning experiences" at the same time...

[smaliden2]

I just started to tig about a month ago when i bought an everlast 205s. Although I cant speak for how long this unit will last I can tell you it has a very smooth arc & very easy to set and control once you understand what each knob does. So from your comments I'm guessing that it seems to be going in my direction! WONDERFUL NEWS!!! I figured if I could learn on the thin stuff (.025) first (total of 8 hours practice so far) that everything else would fall in place. 3/32- 2% lanthenated tungsten, 3/32 filler rod, 40 amps, no pulse, 65% ac balance, 130 ac frequency, 1 sec pre flow, 5 sec post flow, also using the pedal so I can back off as I weld has proven to be very useful and has improved burn through 1000%.
thanks, Scott

[nathan]

Try 1/16" E3 tungsten and 1/16" filler. Low amps like that can struggle to get off of a 3/32". If it's working for you though, I suppose there's no need to change Keep it up man! Try something like that on some 1/8" material and you oughtta be able to lay it right in "no problemo!"