Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
Can you overheat alumimum
Post Reply
User avatar
  • Posts:
  • Joined:
    Wed Jan 22, 2014 11:09 pm

My question is can you overheat a aluminum weld? Some tig welds look like they barely melt it in.... Mine are hotter... Ive always welded on the hot side?

Image
How does this effect the strength? And what if you Re-Heat them?

Sent from my SAMSUNG-SGH-I337 using Tapatalk
Last edited by Wiredwelder on Mon Feb 17, 2014 9:17 pm, edited 1 time in total.
Top
User avatar
  • Posts:
  • Joined:
    Wed Jan 22, 2014 11:09 pm

ImageImageThis was something im working on... Originally I did it with the MIG. Decided to "clean up" the look of my welds.... Went over them with the tig and reheated them. This first one is the weld in question. I know it was a little dirty.

Sent from my SAMSUNG-SGH-I337 using Tapatalk
Attachments
uploadfromtaptalk1392685451680.jpg
uploadfromtaptalk1392685451680.jpg (19.68 KiB) Viewed 1360 times
uploadfromtaptalk1392685435517.jpg
uploadfromtaptalk1392685435517.jpg (24.17 KiB) Viewed 1360 times
Last edited by Wiredwelder on Mon Feb 17, 2014 9:18 pm, edited 1 time in total.
Top
User avatar
  • Posts:
  • Joined:
    Wed Jan 22, 2014 11:09 pm

Im not a pro or a Everyday welder... Just do it for fun when i have a idea or a project... .. Never had formal training. Learned everything I know from welding tips and tricks!!!

Sent from my SAMSUNG-SGH-I337 using Tapatalk
Last edited by Wiredwelder on Mon Feb 17, 2014 9:13 pm, edited 1 time in total.
Top
User avatar
  • Posts:
  • Joined:
    Wed Jan 22, 2014 11:09 pm

These parts go on here... Image
I built the bimini frame... Brackets, and did all the sewing on the sunbrella fabric too.
Image

This was before the fabric was streched tight.
Sent from my SAMSUNG-SGH-I337 using Tapatalk
Top
User avatar
  • Posts:
  • Joined:
    Thu Jan 06, 2011 11:40 pm
  • Location:
    Near New Orleans

You CAN overheat some aluminum welds. 6061T-6, for example, is a hardened material that any welding will affect the properties of. In that case, your goal is to limit heat input when welding to narrow the affected zone as much as possible, and use a filler that will have similar properities when chilled.

Most mild alloys, though, this is not much of an issue.

Steve S
Top
User avatar
  • Posts:
  • Joined:
    Wed Jan 22, 2014 11:09 pm

Thats what i fiured... Just really trying to keep learning and growing with my aluminum work.

I have considered building a boat next.

Sent from my SAMSUNG-SGH-I337 using Tapatalk
Top
Post Reply

Return to “Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding”