I weld mainly with 7018 and 6011 on a stick DC inverter. I also weld with 6013! In my opinion you can run a decent bead with 6013 as long as you have it set right. 6013 gets a bad reputation and is underestimated as well. I would just like to see what kind of beads other people are laying. I would mainly like to see replies that have the following:
- Position
- Machine (settings and polarity)
- Electrode (brand and diameter)
- Material being welded
Thanks everyone and I look forward to starting a positive and productive thread!
findthis_1
- findthis_1
-
New Member
-
Posts:
-
Joined:Sat Jul 09, 2016 10:46 pm
Thanks for the welcome Mike!
Here is something to get this thread going. I will post more pics in the following week when i have a chance to tinker around in my shop. If you have any ideas for something you would like to see let me know and maybe I can do it. Here is a saddle joint pic I had in my phone from an old job. I weld pretty frequently but have not thought to take pictures of any of it but I am going to start now. (with the 6013 anyway).
Forney Easy Weld DC Inverter (Electrode +)
Forney 3/32 6013 Welding Electrode
90 Amps
2 1/2 in. diameter 1/8 thick pipe
Thanks everyone.
Here is something to get this thread going. I will post more pics in the following week when i have a chance to tinker around in my shop. If you have any ideas for something you would like to see let me know and maybe I can do it. Here is a saddle joint pic I had in my phone from an old job. I weld pretty frequently but have not thought to take pictures of any of it but I am going to start now. (with the 6013 anyway).
Forney Easy Weld DC Inverter (Electrode +)
Forney 3/32 6013 Welding Electrode
90 Amps
2 1/2 in. diameter 1/8 thick pipe
Thanks everyone.
- Attachments
-
- 6013 2015.jpg (19.64 KiB) Viewed 2634 times
I'll see if I can use 6013 on some stuff this weekend. I've gotten accustomed to the quick-freeze characteristic of 6010 and 6011. I find 6013 ok, a bit "runny" because of the slow-freezing puddle, but I'm sure it all has to do with settings and technique.
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
Welcome, findthis_1.
A name or nickname we could call you would make conversation easier...
Here's a project I used a lot of 6013 on recently:
http://forum.weldingtipsandtricks.com/v ... f=9&t=9484
Steve S
A name or nickname we could call you would make conversation easier...
Here's a project I used a lot of 6013 on recently:
http://forum.weldingtipsandtricks.com/v ... f=9&t=9484
Steve S
Edgewalker
- Edgewalker
-
Active Member
-
Posts:
-
Joined:Tue Mar 29, 2016 2:12 pm
It's great for thin stuff because of the shallow penetration, and I believe that's what it was designed for.
findthis_1
- findthis_1
-
New Member
-
Posts:
-
Joined:Sat Jul 09, 2016 10:46 pm
My name is Larry. Does anyone know how to change where it says my name? I tried to edit my name but i cannot figure it out. Thanks everyone.
- ldbtx
-
Heavy Hitter
-
Posts:
-
Joined:Thu Jun 13, 2013 12:54 am
-
Location:North Central Texas
-
Contact:
Just leave your username like it is and put your real name at the end of your post. I put "Larry" at the end of mine because that's my name too. 
Larry
Larry
Miller Bobcat 225
Tweco Fabricator 211i
AHP AlphaTIG 200x
Lincoln SP-135+
Hypertherm Powermax 30 Air
ProStar O/A torch
Tweco Fabricator 211i
AHP AlphaTIG 200x
Lincoln SP-135+
Hypertherm Powermax 30 Air
ProStar O/A torch
[IMG]http://
findthis_1
- findthis_1
-
New Member
-
Posts:
-
Joined:Sat Jul 09, 2016 10:46 pm
Great pictures Bugel, That is exactly the kind of stuff I am after ! ! ! Your beads are superb. What rod diameter, machine, amperage, position? I didn't have enough time this weekend to lay any beads. I have an upcoming project that I am really looking forward to posting pics of. Thanks for your contribution to my thread! Take care Bugel