Are you sure it is stainless? If for food industry will there be problems from other alloys that will be used for wear-facing. Brutus aaa for buildup,
Gemini -c possible for hard facing. I would contact rockmount and ask them what they recommend.

http://www.rockmountnassau.com/product1.html