Im pretty sure the amperage is changing as the pedal is changed-just thought some machines show what is being used and it didn't seem like this lincoln ever changed the display

2T or 4T? Not sure my machine has that?

Just a newbie with Tig but thought the amp display on my machine would change as I fluctuate the pedal depression? Mine continues to display the amperage I selected prior to starting. Normal?

Wow...............................you can tell that from a couple crumby welds? Thats exactly what I do. I'm trying to position my forearm differently to avoid that wrist action. It also causes my beads to drop low as I go along (even though I scribe .....occasionally). Could that tilt also be direc...

Great advice! Thank you

.045 filler . Furick gas lense BBW 14 and 16 cup. Bought the Furick beginners kit. No draft. Lincoln Square Wave 200 "factory set" pre and post flow.......ugh........

Thanks alot for the help. Still working on it.

1/8th inch coupon

forgot to mention Furick 16 cup

Not sure if this is an aluminum only area but need some advice on my stainless beads. 30cfm argon, 3/32 lazr tungsten 110 amps on a Lincoln 200 Square wave. Why does the first inch on my beads look like they're a bit hot? At least I'm consistent....................

I'll work on it. Thx for your help!

Torch angle too shallow or too steep? Here's the tungsten grind, I'm guessing 15 degrees. I have noticed that the course wheel I'm grinding it on isn't nearly as nice of finish as the diamond grinder. Does it matter?

is it possible I'm dragging my tungsten in the pool?

What else would cause the stripe, it's in several of my beads.

I appreciate the help! I do on occasion quench the coupons between passes but sometimes think...."just one more", I'll throttle back the pedal a bit. Am currently using a Lincoln Squarewave 200 but have been looking at the primeweld 225. Am I crazy?

Not sure if the attachment went but this is what I'm looking at. Piece of 1/8" DOM scrap

sorry - 03/32 tungsten. I've tried several different sizes of filler (70-2) . Haven't quite figured out how to add a photo, but will eventually. TIA

Mediocre mig and stick welder but am really trying not to become a mediocre Tig welder. I have a Lincoln Square Wave 200 and have been thru 2 bottles of Argon attempting to become a mediocre Tig welder. I’ve watched every (nearly) YouTube video out there and am thoroughly confused. My aluminum beads...

I have seen many videos where the weld looks like "stacked dimes" but mine seem to be the correct height and width but smooth. Lincoln Square Wave 200, 1/8" mild steel, 3/38 Lazr tungsten, 120 amps, 1pps. Ideas?